Merolith R15 spray

1.3 € / kg

Available on backorder

SKU: MH-0005

Weight 30 kg
Dimensions 25 × 25 × 25 cm
Use

Protective coating for reinforcement of polystyrene elements

Method

Spray, in equal layers of 0.5 mm

Packing

10 kg., 30 kg.

Composition

Polymer acrylic binder, marble filler. Does not contain cement

Spray gun requirements

– The nozzle diameter: 2 – 4 mm; – Loading method: top; – Pressure: stable 5-6 atmospheres;

Surface after drying

Smooth

Color

White

Certificate

№ 12.2-18-1 / 16134 from 20.07.2020

Properties

– High adhesion to the foam and extruded polystyrene foam – 0.8 mPa.
– Not hydroscopic Film formed after drying does not pass moisture.
– High elasticity. Due to properly selected high-quality acrylic binder and additives, the composition does not crack during linear expansion (temperature fluctuations), shrinkage of the building and other external factors.
– Adjusted formula for Merolith coating.
– Clean surface after the first coat. После нанесения покрытия распылителем вы получаете поверхность без кратеров, разрывов, пузырьков воздуха. Наносить необходимо аккуратным равномерным слоем в 0,5–1мм 2–3 раза.
– Weather resistance. The content of Merolith compositions, binders, additives, filler make the coating resistant to ultraviolet rays, moisture, low and high temperatures, carbonization, mold…
– Manufacturer’s guarantee for 15 years subject to compliance with the “manual for use” and the use of Merolith mounting materials.

Operational characteristics

– Working temperature with a mixture from +15ºС to +30ºС.
– Drying temperature of parts from +15ºС to +30ºС.
– The density of the coating is 1.4 g / ml.
– Storage temperature from 5ºС to 30ºС. Shelf life 7 months.
– Resistance to cycles “freezing / thawing” – 320 cycles.
– Resistance to temperatures after drying from -40ºС to +60ºС
– Flammability group – G1
– It is made according to DSTU B В.2.7-233:2010

Certificate

№ 12.2-18-1 / 16134 from 20.07.2020