Composition for the reinforcement of expanded polystyrene Merolith D10f

840,00UAH
Product code: MH-0001
Characteristics
  • Polymer acrylic binder, calcite filler. Does not contain cement
  • 30 kg
  • Protective coating for reinforcing facade architectural elements made of polystyrene
  • Broaching on automatic / manual machine

Properties

- High adhesion to the foam cellular plastic and extruded polystyrene foam - 1.2 mPa.
- Not hydroscopic. Film formed after drying does not pass moisture.
- High elasticity. Merolith compositions do not contain cement, therefore in manufacture it is not necessary to use a gauze. It does not give cracks with linear expansion (with temperature fluctuations), shrinkage of the building. Temperature limits allowing bending of parts from +15ºС.
- Hardness. Decorative elements reinforced with Merolith coating have sufficient strength to be used in places where people actively access. The elements can not perform supporting functions.
- Adjusted formula for Merolith coating. When broaching the coating does not drain from the elements, while its density allows you to work at a speed of 5-8 mp / min
- Clean surface after the first coat. Provided the instructions in the manual are followed strictly, it is enough for one broaching to achieve a coating without craters, ruptures, air bubbles or a slight roughness inherent in the facade elements.
- Weather resistance. The content of Merolith compositions, binders, additives, filler make the coating resistant to ultraviolet rays, moisture, low and high temperatures, carbonization, mold…
- Manufacturer's guarantee for 15 years subject to compliance with the "manual for use" and the use of Merolith mounting materials.

Operational characteristics

- Working temperature with a mixture from +15ºC to +30ºС.
- Drying temperature of parts from +15ºC to +30ºС.
- The density of the coating is 1.6 g / ml.
- Storage temperature from +5ºC to +30ºC. Shelf life 7 months.
- Resistance to cycles "freezing / thawing" - 320 cycles.
- Resistance to temperatures after drying from -40ºС to +60ºС
- Flammability group - G1
- It is made according to DSTU B В.2.7-233:2010

Certificate

№05.03.02-04 5765 of 31.01.12

Also we advise to look

Composition for reinforcement of expanded polystyrene Merolith D10q
Composition for the reinforcement of expanded polystyrene Merolith D10
Composition for reinforcement of flexible parts Merolith D4 Flex
Composition for the reinforcement of parts by the Merolith R15 sprayer