Composition for the reinforcement of parts by the Merolith R15 sprayer

1 590,00UAH
Product code: MH-0005
Characteristics
  • Polymer acrylic binder, calcite filler. Does not contain cement
  • 30 kg
  • Protective coating for reinforcement of polystyrene elements
  • Sprayer

Properties

- High adhesion to the foam and extruded polystyrene foam - 0.8 mPa.
- Not hydroscopic Film formed after drying does not pass moisture.
- High elasticity. Due to properly selected high-quality acrylic binder and additives, the composition does not crack during linear expansion (temperature fluctuations), shrinkage of the building and other external factors.
- Adjusted formula for Merolith coating.
- Clean surface after the first coat. После нанесения покрытия распылителем вы получаете поверхность без кратеров, разрывов, пузырьков воздуха. Наносить необходимо аккуратным равномерным слоем в 0,5–1мм 2–3 раза.
- Weather resistance. The content of Merolith compositions, binders, additives, filler make the coating resistant to ultraviolet rays, moisture, low and high temperatures, carbonization, mold...
- Manufacturer's guarantee for 15 years subject to compliance with the "manual for use" and the use of Merolith mounting materials.

Operational characteristics

- Working temperature with a mixture from +15ºС to +30ºС.
- Drying temperature of parts from +15ºС to +30ºС.
- The density of the coating is 1.4 g / ml.
- Storage temperature from 5ºС to 30ºС. Shelf life 7 months.
- Resistance to cycles "freezing / thawing" - 320 cycles.
- Resistance to temperatures after drying from -40ºС to +60ºС
- Flammability group - G1
- It is made according to DSTU B В.2.7-233:2010

Certificate

№05.03.02-04 5765 of 31.01.12

Also we advise to look

Composition for the reinforcement of expanded polystyrene Merolith D10f
Composition for reinforcement of expanded polystyrene Merolith D10q
Composition for the reinforcement of expanded polystyrene Merolith D10
Composition for reinforcement of flexible parts Merolith D4 Flex